MOSIS Process Monitor

The MOSIS Service More than 50,000 designs in 25 years of operation
Processes - Schedule - Prices - Web Forms - Contacts - Site Map
Home --> Technical --> Test Data --> Process Monitor

General Information
About MOSIS
Products
Processes
Prices
Support
User Group
Events
Job Openings
News

Work with MOSIS
Getting Started
Design and Test

Requests
Run Status
Project Status
Test Data

Docs and Forms
Documents
Forms/Agreements
Web Forms

Quick Reference
New Users
Experienced Users
Purchasing Agents
Design and Test
Academic Institutions
Export Program
Submit A Project

MOSIS Process Monitor

C O N T E N T S

1.0 Introduction
2.0 DC Parametric Test Structures
3.0 AC Parametric Test Structures
4.0 Functional Test Structures
5.0 Test Structure Identification
6.0 Test Index

Figure 1: Sample Contact (N+ Active to Metal) Kelvin Bridge
Figure 2: Sample Sheet Resistance Line Width Bridge (Metal1)
Figure 3: Sample Step Coverage (Metal 2 - Metal 3)
Figure 4: Sample (N Enhancement) Common Transistor(s)
Figure 5: Sample (N Enhancement) Isolated Transistor(s)
Figure 6: N_ACT/P_ACT Field Oxide Transistor Pair
Figure 7: Test Inverter(s)
Figure 8: Sample Calibration Capacitor (Floating)
Figure 9: Sample Area Capacitor (POLY to P_PLUS_ACTIVE)
Figure 10: Sample Fringe Capacitor (P_PLUS_ACTIVE to N_WELL)
Figure 11: Functional Test Area
Figure 12: Sample Ring Oscillator (Inverter)

1.0 Introduction

The MOSIS Process Monitor (PM) consists of an array of DC and AC parametric test structures and a small number of functional test devices for monitoring fabrication of wafers by MOSIS foundries. These tests are designed to monitor all of the parameters in the vendor specifications for each supported process.

1.1 PARAMETRIC MONITORS AND PROBING ORGANIZATION: The test structures and tests described here are a basic parametric monitor set. This set is representative of the generic classes of structures required to monitor CMOS wafer fabrication.

There are three classes of test devices: DC parametric, AC parametric, and functional. Each class of test device has its own group of probe card pins. The DC parametric area consists of a 2 x 10 pad group that is tested entirely by instrumentation within a parametric tester. The AC parametric area (capacitors) consists of a 2 x 3 pad group connected through isolation relays to a Hewlett Packard 4275A LCR meter which communicates with the test system through an IEEE-488 interface. The functional device test area consists of a 2 x 10 pad group that connects to an IMS functional test system and an HP frequency counter. Both of these instruments communicate with the parametric test system through an IEEE-488 interface. This functional device test area is configured with pre-assigned pins to simplify functional tester programming and interfacing. Pin assignments for the functional pad group are included in section 1.4, Functional Test Structures.

Probe pads are 80 µm square on a 160-µm pitch.

The set of test structures described in this document is a library for designing PMs for particular requirements. MOSIS technologies that use full wafer masks have a rich set of structures in a full die dropin PM; with reticle (step and repeat) masks a minimal set of test structures are placed in a small test strip. In either case, wafer monitoring (or selection) requires at least the following measurements:

INTERCONNECT PARAMETERS:

Contact Resistance
Contact Voltage Sum (rectifying)
Sheet Resistance (metal, poly, and active areas)
Delta Line Width (metal and poly)

STEP COVERAGE:

Comb Isolation (metal and poly)
Serpentine Continuity

TRANSISTOR CHARACTERISTICS:

Transistor Threshold Voltage
Process Gain, Kp (beta/2)
Gamma (body effect coefficient)
Delta Length, Delta Width
Saturation Current
Channel Punch-through Voltage
Junction Breakdown
Gate Oxide Thickness

FIELD OXIDE TRANSISTORS:

Threshold

INVERTERS:

Vout, high
Vout, low
Inverter Threshold (Vinv)
Gain at Inverter Threshold

CAPACITORS:

Area Capacitance
Fringe Capacitance

RING OSCILLATOR:

Frequency

2.0 DC Parametric Test Structures

2.1 CONTACT RESISTANCE BRIDGES

The contact resistance bridges are Kelvin-connected contact resistors with a single (nominal design rule) contact between two connected layers on the chip. Two variations of contact resistors are available: one with large overlap around the contact, and the other with minimum overlap allowed by the design rules. The contact resistor with the large overlap is used to measure the interfacial resistance of the contact itself. Contacts with minimum overlap have an additional resistance component caused by current crowding within the minimum overlap region.

For large overlap contacts, the upper layer is run in a 'dogleg' (bent 90 degrees in the center) bar of 15 µm width with a minimum contact (or via) placed in the center of the right angle jog. The connected layer is constructed with an identical structure rotated 180 degrees with the center overlapping the metal. The width of this layer is also 15 µm. The ends of the four bars are each connected to separate probe pads.

Minimum overlap contacts are constructed by replacing the center overlap region of the large overlap contact with a minimum overlap contact structure, connected to the 15 µm width bars with a short length of minimum design rule width wire.

See Figure 1: Sample Contact (N+ Active to Metal) Kelvin Bridge

2.1.1 TESTING

Testing is performed by passing constant current through the contact between the two layers and measuring the resulting voltage. The constant current source is attached to two opposite arms (different layers) of the bridge and the resulting voltage is measured between the remaining two arms. With the current source at zero, the thermal voltage in the test structure is measured and later subtracted from the measured voltage. Current is passed in two directions and the measured voltages are summed (preserving the sign) to determine if the contact is partially rectifying.

The resistance measured with the current in the positive direction and the voltage sum are reported.

Resistance: R = VMEASURE / IFORCE

Voltage Sum: VSUM = V(+IFORCE) + V(IFORCE)

IFORCE = 1.0 mA for cuts (M1/P+, M1/N+, M1/Poly), 10.0 mA for vias (M1/M2, M2/M3)

2.2 SHEET RESISTANCE - LINE WIDTH BRIDGES (Electrical Line Width and Sheet Resistance)

Sheet resistance and electrical line width are measured using a bridge test structure consisting of a Van der Pauw crossed bridge for sheet resistance measurement and a Kelvin line width measurement section. The Van der Pauw section is the classic four-arm structure used in the industry for many years, with arm widths of 25 µm. The tap distances on the wire width section are determined by the design rule wire pitch. The wire width section has a width equal to 2 * (minimum wire width) + (minimum wire spacing). The sheet resistance-line width bridges occupy four pad pairs and are constructed in every conducting layer in a technology.

See Figure 2: Sample Sheet Resistance Line Width Bridge (Metal1)

2.2.1 TESTING

Testing consists of two parts taken in the order: Van der Pauw (Rs); wire width. The Van der Pauw test is performed first because the sheet resistance obtained from this portion of the test is used in the wire width determination.

The Van der Pauw measurement is done by passing constant current through two adjacent arms of the crossed bridge and measuring voltage on diagonal pairs of arms. The measurement is repeated with the pairs of arms for current force and for voltage sense rotated 90 degrees on the crossed bridge. The two voltage readings are averaged to remove any asymmetry in the bridge.

Wire width measurements are taken by passing constant current through the entire length of the structure and measuring the voltage between the taps on the wire.

Sheet resistance is computed from:: RS = (pi/ln 2) * (AVG_VMEASURE / IFORCE) ohms/square
where: AVG_VMEASURE = (VMEASURE1 + VMEASURE2) / 2; pi = 3.1415927; ln is the natural logarithm; IFORCE =
75 mA for Metal2, Metal3, Metal4
40 mA for Metal1
1.0 mA for Active and Poly
200 µA for Well
The line width is computed from:: Weff = (RS * L) / (VB / IFORCE) µm
where: L = drawn wire bridge tap spacing (120 µm); VB = measured wire bridge tap voltage; IFORCE =
40 mA for Metal2, Metal3, Metal4
15 mA for Metal1
100 µA for active area and poly
Width Error is computed as follows:: W_error = W - W_drawn,
where: W_drawn is as indicated in the text above.

Sheet resistance and line width computations are carried out in the MOSIS wafer electrical test report generator rather than at probe time.

2.3 STEP COVERAGE TEST STRUCTURE

The step coverage test structure monitors metal coverage over topology steps through wire continuity and comb isolation. The structure is intended to be used to detect major process failures. In general there are not likely to be many failures due to poor metal step coverage on a structure of such a small area.

The step coverage structures can include: Poly, Metal1, Metal2, Metal3, and Metal4. The Poly geometry consists of serpentine polysilicon between interdigitated fingers of Poly running over oxide steps of active area at minimum design rule width and spacing. The Metal1 geometry consists of Metal1 over Poly and Active. The Metal2 geometry has Metal2 over Metal1, Poly, and Active. Metal3 and Metal4 geometry continue this pattern. The structures are usually paired, where each portion of the structure occupies half of the available space.

See Figure 3: Sample Step Coverage (Metal 2 - Metal 3)

2.3.1 TESTING

Testing the step coverage structure involves measuring the serpentine structure for continuity and measuring the interdigitated structures for electrical shorts.

The continuity test consists of current (IFORCE = 10 mA) forced through the serpentine with a voltage measurement to calculate a resistance. Note that an open circuit in the serpentine is easily detected by setting a voltage compliance limit on IFORCE and observing if the voltage limit is reached. Electrical shorts in the interdigitated structures are detected by applying a voltage (VFORCE = process Vdd) between the serpentine and the comb and measuring the resulting current.

The parametric tester logs the voltage for the continuity test and the current for the short test. At this time the wafer electrical test summary report includes only the measured current.

2.4 THIN OXIDE TRANSISTOR STRUCTURES (N and P)

The test transistors are organized in several groups, generally along the lines of variable length, fixed width; fixed length, variable width; and others. Transistor channel geometries are listed by test vehicle in the appendix and are generated in both N channel and P channel.

These sizes are intended for use in full characterization of the transistor process targets and for extraction of device model parameters. A selected subset of transistor sizes makes up the minimum set of transistors necessary for wafer acceptance. The closed (edgeless) device is intended for evaluation of radiation hardness.

See:

Figure 4: Sample (N Enhancement) Common Transistor(s)
Figure 5: Sample (N Enhancement) Isolated Transistor(s)

2.4.1 TESTING

2.4.1.1 Tests performed on transistors are:

TRANSISTOR THRESHOLD VOLTAGE

Threshold voltages (Vth) are obtained from a conductivity curve which is a plot of drain current versus gate voltage for a drain voltage that is much less than twice the Fermi potential (2 * phi). The absolute drain voltage is set at 50 mv. Threshold voltage is found by extrapolating the linear portion of the conductivity curve to Ids = 0. The intersection of the extrapolated line is defined as the threshold voltage. Measurements are made using at least three different body voltages (0, Vdd/2, and Vdd).

PROCESS GAIN FACTOR

The slope of the conduction curve obtained in the threshold voltage measurement process is used to calculate the process gain factor (K') The slope (S) of the conduction curve is 2 * K * Vd. Therefore,

K = S / (2 * Vd).

Since K = K'* (W / L), then the process gain factor is calculated from K' =(S/(2*Vd))*(L/W).

(Note: W and L must be corrected for as-fabricated W and L, where W = W_drawn - DW, and L = L_drawn - DL.

Derivation of W (effective) and L (effective) is discussed in the EFFECTIVE CHANNEL WIDTH/LENGTH section of this document.)

BODY EFFECT

The change in voltage threshold due to source-to-substrate (body) reverse bias is obtained from measurements of voltage threshold at different body reverse biases. Threshold voltages are measured at three different body voltages (0, Vdd/2, Vdd; negative relative to source for N channel devices and positive relative to source for the P channel devices). Threshold voltages are measured in the manner described above.

GAMMA (SPICE Body Effect Parameter) is assumed to be defined by the SPICE body effect relationship:

Vt = Vt(0) + GAMMA*{SQRT(ABS(Vsb) + 2*PHI_F) SQRT(2*PHI_F)}

Taking two threshold measurements at different body voltages, GAMMA can be calculated by taking the difference between the two measured threshold voltages and solving for GAMMA:

GAMMA = [ABS(Vt(2)) ABS(Vt(1))] / D

where,

D = SQRT{ABS(Vsb(2)) + 2*PHI_F} SQRT{ABS(Vsb(1)) + 2*PHI_F},

and

2*PHI_F is assumed to be 0.7 for silicon technologies.

SATURATION CURRENT

Saturation current is measured by connecting the gate to the drain (body connected to source) and applying Vgs = Vds = process Vdd and measuring current (Idss).

PUNCH-THROUGH VOLTAGE

This test is performed on short channel devices. The punch-through voltage is measured by using a ramp search method in which an applied drain voltage (10 V maximum) is increased monotonically while monitoring the drain current. The ramp voltage is logged as punch-through voltage (Vpt) when a specified drain current flows (10 nA per µm channel width). The drain is connected to a voltage supply (Vds) which is in series with a current meter; gate, source and bulk are connected to ground. As a further check, the gate and source are left open while a current meter is connected between the bulk and ground. The same ramp test is performed to determine if the measured Vpt actually represents junction breakdown.

2.4.1.2 Tests performed on selected transistors include:

TRANSISTOR I/V CURVES

A selected set of transistors will be used to collect I/V curves for SPICE model parameters. Drain current (Ids) measurements will be made at various drain-source voltages (Vds), gate-source voltages (Vgs) and bulk-source voltages (Vbs). The specific set of transistor geometries and sets of bias voltages will be determined by the requirements of the parameter extractor. The temperature of the vacuum chuck at the time of the test is logged in the measurement data file.

ACTIVE AREA JUNCTION LEAKAGE

Junction leakage current is measured at a junction potential of process Vdd. Source/drain-to-well junction leakage is measured with the well connected to the bulk. Junction leakage is measured on the drain of large, square transistor with the gate and source floating. For increased sensitivity, junction leakage current can be measured on the junction capacitor structures.

ACTIVE AREA JUNCTION BREAKDOWN

Junction breakdown is measured by applying a reverse bias current of 1.0 µA (positive for N junctions and negative for P junctions) and measuring the resulting junction voltage. Source/drain-to-well junction breakdown is measured with the well connected to the bulk. Measurements are made on a large, square transistor using the drain junction with the source and gate floating.

DRAIN/SOURCE LEAKAGE

Measurements are made with the gate connected to the source and a picoammeter connected between source and ground; bulk is connected to a specified Vbs (currently 0 V). The transistor used in this measurement should a transistor with minimum design rule channel length and with the largest channel width included within the process monitor. Leakage current measurements are then normalized per micrometer of channel width.

EFFECTIVE CHANNEL WIDTH/LENGTH

Effective channel width and length are extracted by extrapolation of the measured channel conductance to find delta W and delta L. Values for effective channel length and width are obtained by adding the delta length and delta width values to the drawn length and width.

Delta Channel Length: DL = (L1*S1 L2*S2) / (S1 S2),: for transistors with: W1 = W2
Delta Channel Width: DW = (W1*S2 W2*S1) / (S2S1),: for transistors with: L1 = L2
where: S1 = linear region slope of the larger device; S2 = linear region slope of the smaller device; L1 = drawn device length, larger device; L2 = drawn device length, smaller device; W1 = drawn device width , larger device; W2 = drawn device width, smaller device
Note:: L_effective = L_drawn - DL; W_effective = W_drawn - DW

2.5 THICK (FIELD) OXIDE TRANSISTORS

Thick oxide transistors consist of minimum active to active regions with the gap between them covered by Metal1, Metal2 or Poly. In addition, a thick oxide transistor may be constructed with P-well (or N-well) to P+ regions (or N+ regions) at minimum spacing, covered by Metal1, Metal2, or Poly. In this test device the P-well is the source.

See Figure 6: N_ACT/P_ACT Field Oxide Transistor Pair

2.5.1 TESTING: The threshold of the thick oxide devices is measured by using a search method in which an applied gate voltage is found such that a specified drain current flows. The drain is connected to a specified voltage (process Vdd), the source is connected to a current meter, and the bulk is connected to ground. A separate gate supply is connected to the gate terminal. The gate supply voltage is varied in a binary search pattern to find the gate voltage that will cause the drain current to be 1.0 µA. The resulting gate voltage is reported as the threshold.

2.6 VARIABLE RATIO INVERTERS

Inverters constructed with minimum channel length P- and N-channel transistors are contained in a group with common Vdd, ground, and input connections, separate outputs, and with width ratios of 1.0, 1.5, 2.0.

See Figure 7: Test Inverter(s)

2.6.1 TESTING: Each inverter is tested with Vdd set at the nominal operating voltage for the technology. The output voltage is measured with the input connected to Vdd and ground and with the output connected to a 100 µA constant current load. Vout,high is measured with 100 µA to ground. Vout,low is measured with 100 µA to Vdd. The input is connected to the output and the resulting stable voltage is identified as the inverter threshold (Vinv). Finally the gain of the inverter is measured at an input voltage of Vinv.

3.0 AC Parametric Test Structures

At present, the only AC parameters monitored are the interlayer capacitances. Transistor small signal characteristics may be monitored in the future.

The capacitor array consists of area capacitors (small perimeter), fringe capacitors (large perimeter), and gate overlap capacitors. For each capacitance reported, the capacitance measurements require data reduction to produce the desired information (e.g., extraction of the area and fringe components of capacitance). This data reduction is done in the MOSIS report generator.

All capacitors are designed to fit into the 2 x 10 pad block height of 240 µm. The lengths of the capacitor structures may be varied to obtain the desired capacitance, but are currently fixed at 300 µm. A full four point electrical structure is maintained to maximize the accuracy available from a general purpose LCR meter.

Capacitors that have one electrode connected to the well (either P-well or N-well) have a substrate-to-well strap to assure that the stray capacitance can be compensated by a null capacitor.

3.1 NULL CAPACITORS (Calibration Capacitors)

Three six-pad null capacitors are used for measuring the stray capacitances associated with the test environment (fixture plus probe pads and test structure interconnects), which are subtracted from each raw measured capacitance value during data processing. The floating calibration capacitor measures stray capacitance associated with capacitors which have neither electrode connected to the substrate (e.g., a Metal2 to Metal1 capacitor). One electrode of the substrate-connected calibration capacitor is connected to the substrate to measure stray capacitance associated with capacitors that use the substrate as one electrode (e.g., Metal2 to substrate). The shield-substrate calibration capacitor connects the LCR meter cable shields to the wafer substrate in order to remove the effective substrate-connected parasitic capacitance associated with gate overlap, net-to-net, and crossover capacitors.

See Figure 8: Sample Calibration Capacitor (Floating)

3.2 AREA CAPACITORS

The area capacitors are designed with the top electrode dimensions set at 240 µm high by 300 µm wide. This provides at least 2.0 pF capacitance from the field oxide capacitors.

See Figure 9: Sample Area Capacitor (POLY to P_PLUS_ACTIVE)

3.2.1 TESTING

Measurements are made with an AC test voltage of 100 mV rms and a frequency of 100 KHz.

Thin oxide capacitor measurements for determining gate oxide thickness are taken in both strong inversion and accumulation of the oxide semiconductor interface (V_gate = process Vdd). The value taken from the measurement in strong inversion is normally used for modeling and other applications.

All other capacitors are tested at zero bias voltage. (Modeling data sets include C-V data for both gate and junction capacitors.)

Geometrical parameters are:: Area: Aa = H * L µm²; Perimeter: Pa = (2 * H) + (2 * L) µm
where: H = top electrode height; L = top electrode length
Thin oxide capacitor measurements are used in the computation of the oxide thickness with the following equation:: Tox = (Aa * 3.45E-11) / Cam
where: Cam = measured capacitance of the area capacitor; 3.45E-11 = permittivity of silicon dioxide
Interlayer dielectric capacitance measurements can be used to calculate the thickness of the insulator by using the above equation if the interlayer dielectric is silicon dioxide (dielectric constant = 3.9). If the dielectric is some other material (e.g., silicon nitride or a combination of silicon dioxide and silicon nitride) the more general form of the equation must be used:: Tins = Er * E0 * (Aa / Cam)
where: Er = relative dielectric constant of the insulator; E0 = permittivity of free space = 8.854E-12 farads/meter

3.3 FRINGE CAPACITORS

The fringe capacitors are comb structures with a comb width of 10 µm and a comb spacing of 10 µm. The height is slightly smaller than 240 µm, the maximum height permitted by the capacitor structures. Top electrode length is 300 µm.

See Figure 10: Sample Fringe Capacitor (P_PLUS_ACTIVE to N_WELL)

3.3.1 TESTING

Measurements are made with an AC test voltage of 100 mV rms and a frequency of 100 KHz.

Capacitors with thin oxide between the layers are measured at zero volts bias and with LCR meter shields connected to the substrate to obtain the gate overlap capacitance.

All other capacitors are tested at zero bias voltage. (Modeling data sets include C-V data for both gate and junction capacitors.)

Geometrical parameters are:: Area: Af = (NR * H * 10) + ((NR - 1) * 10 * 10) µm²; Perimeter: Pf = (H * 2) + (NR * 2 * 10) + ((NR - 1) * 2 * H) µm
where: NR = INT( L / 20 ); H = top electrode height; L = top electrode length

Computation of component capacitances (e.g., junction: CJSW and CJ) using the area capacitor measurements and the fringe capacitor measurements is carried with the following equations:

Fringe capacitance:: Cf = ((Cam/Aa) - (Cfm/Af)) / ((Pa/Aa) - (Pf/Af)) aF/µm
Area capacitance:: Ca = (Cam/Aa) - Cf * (Pa/Aa) aF/µm²
where: Cam = measured capacitance of the area capacitor; Cfm = measured capacitance of the fringe capacitor

4.0 Functional Test Structures

The functional test structures are used to evaluate the performance of the extracted model parameters and to act as an alarm for a low yield wafer lot.

The functional test area is configured so that the pinout is standardized to minimize the complexity of the interface to test equipment. This pinout is defined assuming the following pin numbering convention:

See Figure 11: Functional Test Area

The Input/Output pins and the Clock are interfaced with tri-state I/O pins on the functional tester. Pin 12 is also connected to a small relay that can connect the ring oscillator ENABLE signal to this pin. The purpose of the relay is to reduce the stray capacitance associated with the ENABLE signal wire.

4.1 RING OSCILLATOR

The Ring Oscillator in the MOSIS process Monitor is used to serve as a very simple benchmark performance measure of the various foundry technologies supported by MOSIS. It also serves as one of the functional devices for verifying the accuracy of circuit simulations that use the MOSIS extracted SPICE model parameters.

By simulating a design using MOSIS model parameters from several wafer lots, a design can be tested for performance over past fabricated lots. Since typical foundries are fairly stable, then simulations using past history are useful for providing an estimate of what performance to expect in future wafer lots. Model parameters for each wafer lot are tested by simulating inverter and ring oscillator circuits fabricated in the MOSIS process monitor on each wafer lot. The simulation versus measured error must be less than 10% to have the model parameters be acceptable for MOSIS to post them in the wafer lot Parametric Test Results. If the model parameters fail to meet this requirement, then the measured I-V data is re-analyzed (or new data is collected) and a new set of model parameters are optimized and tested as indicated above.

The Ring Oscillator consists of a string of 31 simple inverters that form the ring oscillator. No attempt is made to construct the ring oscillator using one of the many cell library inverters or gates. The layout is intentionally very compact to cause the ring oscillator frequency performance to be dominated by the transistors. Device channel lengths used for ring oscillator are minimum design rule channel length, which is (2 * lambda). The standard width for NMOS device is (4 * lambda) and (8 * lambda) for PMOS. One inverter stage of the ring oscillator is replaced with a 2-input NAND gate, which serves as an externally controlled trigger to prevent multi-mode oscillation from occurring during power-up. The ring oscillator output is isolated with a buffer and then is connected to a divide by 256 counter (or a 1024 counter for 0.25 µm technology and smaller) to reduce the output frequency. Reducing the output frequency permits using the parametric test system pin matrix, directing the ring oscillator frequency divided output to a frequency counter during wafer probe. The output of the frequency divider is buffered for output onto a highly capacitance loaded measuring system. Frequency measurements from the frequency counter are multiplied by the above counter stage size in order to report the actual 31- stage ring oscillator frequency in the MOSIS Parametric Test Results.

The ring oscillator layout is configured to separate the power supply for the 31-stage ring oscillator from the divider/output buffer so we are able to obtain accurate power measurements. The measured ring oscillator frequency obtained in the manner above, along with the power supply current to the 31-stage ring oscillator is used to calculate the reported per stage power in uw/MHz/gate.

In some technologies, a second ring oscillator will be added to the MOSIS Process Monitor in order to measure the performance of different transistor types (such as the thick gate oxide option from TSMC) or to assess the effects of channel narrowing (such as in the AMI C5N 0.5 µm). In the case of the C5N (0.5 µm), the transistors in the inverters are (10 * lambda) width for NMOS and (20 * lambda) width for PMOS (L is still 2 lambda). The ring oscillator frequency and power using these larger width devices is higher than the standard width devices. This difference is because the effect of channel narrowing is a smaller percentage of the layout width and because the wider devices can drive larger current to overcome the effects of the small parasitic capacitance external to the transistors.

See Figure 12: Sample Ring Oscillator (Inverter)

4.1.1 TESTING: The parametric tester supplies power (Vdd and ground) to the device under test through the probe card interface board. A relay is activated to connect a parametric tester pin to the ring oscillator enable pin and a disable voltage level is applied to suppress any multimode oscillation that may be present. The disable voltage is removed to start oscillation and a frequency measurement is taken.
The parametric test system reports the average of two consecutive frequency measurements in which the second reading is within 10% of the first. Up to five readings are taken until the above condition is achieved. If acceptable readings are not found then the structure is considered inoperative.

4.2 YIELD MONITOR

The yield monitor is a set of n-element shift registers where n is determined by the MOSIS test layout generator and is a function of the total area allocated to the circuit. Current designs have either 10 or 14 channels, each with n elements.

4.2.1 TESTING: Yield monitor testing is performed with a functional tester that operates independently from the parametric tester. The functional tester supplies power (Vdd and ground) to the device under test through the probe card interface board. A device is considered functional if it passes (shifts) logic 1 and logic 0 inputs on each channel to the outputs after an appropriate number of clock cycles.

5.0 Test Structure Identification

MOSIS process monitor test structure layouts include a reference designator to help locate a particular structure within the process monitor. The following tables list the test structure names and their corresponding reference designators.

Capacitors Test Block Title Designator Notes

Crossover Capacitor METAL2 to METAL1 C1 Not used

Crossover Capacitor METAL 1 to POLY C2 Not used

Edge Capacitor POLY to POLY C3 Not used

Edge Capacitor METAL2 to METAL2 C4 Not used

Edge Capacitor METAL1 to METAL1 C5 Not used

Fringe Capacitor POLY to N_PLUS_ACTIVE C6

Fringe Capacitor POLY to P_PLUS_ACTIVE C7

Fringe Capacitor N_PLUS_ACTIVE to P_WELL C8

Fringe Capacitor P_PLUS_ACTIVE to N_WELL C9

Area Capacitor METAL2 to POLY C10

Area Capacitor METAL1 to POLY C11

Area Capacitor METAL2 to METAL1 C12

Area Capacitor METAL2 to N_PLUS_ACTIVE C13

Area Capacitor METAL1 to N_PLUS_ACTIVE C14

Area Capacitor METAL2 to N_WELL C15

Area Capacitor METAL1 to N_WELL C16

Area Capacitor POLY to N_WELL C17

Area Capacitor N_PLUS_ACTIVE to P_WELL C18

Area Capacitor P_PLUS_ACTIVE to N_WELL C19

Area Capacitor POLY to N_PLUS_ACTIVE C20

Area Capacitor POLY to P_PLUS_ACTIVE C21

Calibration Capacitor with connected substrate C22

Calibration Capacitor floating C23

Area Capacitor ELECTRODE* to POLY C30 * Second Poly

Area Capacitor METAL1 to ELECTRODE* C31

Area Capacitor METAL2 to ELECTRODE* C32

Area Capacitor ELECTRODE* to N_PLUS_ACTIVE C33

Area Capacitor ELECTRODE* to P_PLUS_ACTIVE C34

Area Capacitor ELECTRODE* to P_WELL C35

Fringe Capacitor ELECTRODE* to N_PLUS_ACTIVE C36

Fringe Capacitor ELECTRODE* to P_PLUS_ACTIVE C37

Edge Capacitor ELECTRODE* to ELECTRODE* C38 Not used

Fringe Capacitor METAL1 to P_WELL C39

Fringe Capacitor METAL2 to P_WELL C40

Fringe Capacitor METAL1 to POLY C41

Fringe Capacitor METAL2 to POLY C42

Area Capacitor METAL3 to P_WELL C43

Area Capacitor METAL3 to N_PLUS_ACTIVE C44

Area Capacitor METAL3 to METAL2 C45

Area Capacitor METAL3 to POLY C46

Fringe Capacitor METAL3 to P_WELL C47

Fringe Capacitor METAL3 to POLY C48

Edge Capacitor METAL3 to METAL3 C49 Not used

Crossover Capacitor METAL3 to METAL2 C50 Not used

Fringe Capacitor POLY to P_WELL C51

Fringe Capacitor ELECTRODE* to P_WELL C52

Fringe Capacitor METAL1 to N_PLUS_ACTIVE C53

Fringe Capacitor METAL2 to N_PLUS_ACTIVE C54

Fringe Capacitor METAL3 to N_PLUS_ACTIVE C55

Fringe Capacitor METAL2 to METAL1 C56

Fringe Capacitor ELECTRODE* to POLY C57

Fringe Capacitor METAL1 to ELECTRODE* C58

Fringe Capacitor METAL2 to ELECTRODE* C59

Fringe Capacitor METAL3 to METAL2 C60

Area Capacitor METAL3 to METAL1 C61

Fringe Capacitor METAL3 to METAL1 C62

Area Capacitor POLY to CAP_WELL** C63 ** HP Linear Cap

Fringe Capacitor POLY to CAP_WELL** C64

Area Capacitor POLY to CAP_IMPLANT** C65

Calibration Capacitor with connected shield C66

Functional devices Test Block Title Designator Notes

Dynamic Shift Register F1 Not used

Pattern Generator F2 Not used

Ring Oscillator F3

XOR tree F4 Not used

Ring Oscillator trio F6

Ring Oscillator pair F7

Divided-by-four Ring Oscillator F8

Shift Register Yield Monitor (rev 2) F10

Shift Register Yield Monitor (rev 4) F11

Inverter Ring Oscillator F12

Nand2 Ring Oscillator F13

Nor2 Ring Oscillator F14

Non-feature-size Ring Oscillator F15

Non-feature-size Divided-by-four Ring Oscillator F16

Inverters Test Block Title Designator Notes

Test inverter(s) I1

Sheet and contact resistance bridges Test Block Title Designator Notes

Poly (P+) bridge K1

Poly (N+) bridge K2

P+ Active bridge K3

N+ Active bridge K4

Metal bridge K5

Second_metal bridge K6

P-Well bridge K7

N-Well bridge K8

P+ Active to Metal contact K9

Second Metal to First Metal contact K10

Poly bridge K11

Poly (P+) to Metal contact K12

Poly (N+) to Metal contact K13

N+ Active to Metal contact K14

P-Well under Poly bridge K15

N-Well under Poly bridge K16

Electrode* bridge K20 * Second Poly

Electrode* to Metal contact K21 * Second Poly

Third Metal to Second Metal contact K23

Third_metal bridge K24

N-Ldd bridge K25

P-Ldd bridge K26

Second Metal to First Metal contact over Poly K27

Second Metal to First Metal contact over Active K28

Third Metal to Second Metal contact over Active K29

Third Metal to Second Metal contact over Poly K30

Third Metal to Second Metal contact over Metal1 K31

Third Metal to Second Metal contact over Poly and Metal1 K32

Poly (P+) to Metal contact (min overlap) K33

Poly (N+) to Metal contact (min overlap) K34

N+ Active to Metal contact (min overlap) K35

P+ Active to Metal contact (min overlap) K36

Contact string K37

Poly (non silicided) bridge K38

Poly (non silicided) to Metal contact K39

Step coverage Test Block Title Designator Notes

Step coverage METAL1 METAL2 S1

Step control METAL1 METAL2 S2

Step coverage METAL2 S3

Step control METAL2 S4

Step coverage METAL1 S5

Step control METAL1 S6

Step coverage METAL2 METAL3 S7

Step control METAL2 METAL3 S8

Step coverage METAL3 S9

Step control METAL3 S10

Step coverage POLY METAL1 S11

Step control POLY METAL1 S12

Step coverage POLY S13

Step control POLY S14

Poly (N/P) bridging test structure S15

Transistors Test Block Title Designator Notes

N_ENHANCEMENT common transistor(s) T1

P_ENHANCEMENT common transistor(s) T2

N_ACT field oxide transistors T3

P_ACT field oxide transistors T4

N_ENHANCEMENT isolated transistor(s) T5

P_ENHANCEMENT isolated transistor(s) T6

N_ENHANCEMENT closed transistor T7

P_ENHANCEMENT closed transistor T8

N_ACT field oxide (REVISED) transistors T12

P_ACT field oxide (REVISED) transistors T13

N_ACT / P_ACT field oxide (REVISED) transistor pair T14

NPN common transistor(s) T15

N_ACT field oxide (NEW) transistors T16

P_ACT field oxide (NEW) transistors T17

N_ACT / P_ACT field oxide (NEW) transistor pair T18

N_LDD_ENHANCEMENT isolated transistor(s) T19

P_LDD_ENHANCEMENT isolated transistor(s) T20

N_POLY2_ENHANCEMENT* common transistor(s) T21 * Second Poly

P_POLY2_ENHANCEMENT* common transistor(s) T22 * Second Poly

N_POLY2_ENHANCEMENT* isolated transistor(s) T23 * Second Poly

P_POLY2_ENHANCEMENT* isolated transistor(s) T24 * Second Poly

6.0 Test Index

INTERCONNECT PARAMETERS

Contact Resistance Structure Designator Test Reference Section

N+ Active to M1 K14 2.1

P+ Active to M1 K9

Poly (N+) to M1 K13

Poly (P+) to M1 K12

M2 to M1 (Field) K10

M2 to M1 (Poly) K27

M2 to M1 (Active) K28

M3 to M2 (Field) K23

M3 to M2 (Poly) K29

M3 to M2 (Active) K30

M3 to M2 (Metal1) K31

M3 to M2 (Poly, Metal1) K32

Poly (P+) to M1 (Min. Overlap) K33

Poly (N+) to M1 (Min. Overlap) K34

N+ Active to M1 (Min. Overlap) K35

P+ Active to M1 (Min. Overlap) K36

Contact String K37

Poly (non-silicided) to M1 K39

Electrode* to M1 K21 * Second Poly

Voltage Sum (rectifying) Structure Designator Test Reference Section

N+ Active to M1 K14 2.1

P+ Active to M1 K9

Poly (N+) to M1 K13

Poly (P+) to M1 K12

Sheet Resistance Structure Designator Test Reference Section

Poly (P+) K1 2.2

Poly (N+) K2

P+ Active K3

N+ Active K4

Metal1 K5

Metal2 K6

P-Well K7

N-Well K8

Poly K11

P-Well under Poly K15

N-Well under Poly K16

Electrode* K20 * Second Poly

Metal3 K24

N-Ldd K25

P-Ldd K26

Poly (non silicided) K38

Delta Line Width Structure Designator Test Reference Section

Poly (P+) K1 2.2

Poly (N+) K2

P+ Active K3

N+ Active K4

Metal1 K5

Metal2 K6

P-Well K7

N-Well K8

Poly K11

P-Well under Poly K15

N-Well under Poly K16

Electrode* K20 * Second Poly

Metal3 K24

N-Ldd K25

P-Ldd K26

Poly (non silicided) K38

Step Comb Isolation Structure Designator Test Reference Section

Step coverage Metal1 Metal2 S1 2.3

Step control METAL1 METAL2 S2

Step coverage METAL2 S3

Step control METAL2 S4

Step coverage METAL1 S5

Step control METAL1 S6

Step coverage METAL2 METAL3 S7

Step control METAL2 METAL3 S8

Step coverage METAL3 S9

Step control METAL3 S10

Step coverage POLY METAL1 S11

Step control POLY METAL1 S12

Step coverage POLY S13

Step control POLY S14

Poly (N/P) bridging test structure S15

Step Serpentine Continuity Structure Designator Test Reference Section

Step coverage Metal1 Metal2 S1 2.3

Step control METAL1 METAL2 S2

Step coverage METAL2 S3

Step control METAL2 S4

Step coverage METAL1 S5

Step control METAL1 S6

Step coverage METAL2 METAL3 S7

Step control METAL2 METAL3 S8

Step coverage METAL3 S9

Step control METAL3 S10

Step coverage POLY METAL1 S11

Step control POLY METAL1 S12

Step coverage POLY S13

Step control POLY S14

Poly (N/P) bridging test structure S15

Document last updated: January 19, 2002

Related Links

Fabrication Schedule

Customer Support

MOSIS Products

Looking for something special? Check our Site Map or Search MOSIS.

The MOSIS Service
4676 Admiralty Way
Marina del Rey, California 90292-6695 USA
Contact MOSIS

Privacy Statement

C O N T E N T S

1.1 PARAMETRIC MONITORS AND PROBING ORGANIZATION

INTERCONNECT PARAMETERS:

STEP COVERAGE:

TRANSISTOR CHARACTERISTICS:

FIELD OXIDE TRANSISTORS:

INVERTERS:

CAPACITORS:

RING OSCILLATOR:

2.1 CONTACT RESISTANCE BRIDGES

2.1.1 TESTING

2.2 SHEET RESISTANCE - LINE WIDTH BRIDGES (Electrical Line Width and Sheet Resistance)

2.2.1 TESTING

2.3 STEP COVERAGE TEST STRUCTURE

2.3.1 TESTING

2.4 THIN OXIDE TRANSISTOR STRUCTURES (N and P)

2.4.1 TESTING

2.4.1.1 Tests performed on transistors are:

TRANSISTOR THRESHOLD VOLTAGE

PROCESS GAIN FACTOR

BODY EFFECT

SATURATION CURRENT

PUNCH-THROUGH VOLTAGE

2.4.1.2 Tests performed on selected transistors include:

TRANSISTOR I/V CURVES

ACTIVE AREA JUNCTION LEAKAGE

ACTIVE AREA JUNCTION BREAKDOWN

DRAIN/SOURCE LEAKAGE

EFFECTIVE CHANNEL WIDTH/LENGTH

2.5 THICK (FIELD) OXIDE TRANSISTORS

2.5.1 TESTING

2.6 VARIABLE RATIO INVERTERS

2.6.1 TESTING

3.1 NULL CAPACITORS (Calibration Capacitors)

3.2 AREA CAPACITORS

3.2.1 TESTING

3.3 FRINGE CAPACITORS

3.3.1 TESTING

4.1 RING OSCILLATOR

4.1.1 TESTING

4.2 YIELD MONITOR

4.2.1 TESTING

INTERCONNECT PARAMETERS